Polycarboxylate Superplasticizer (Slump retaining)

Polycarboxylate Superplasticizer (Slump retaining)

  • Description
  • Inquiry

This product is a new generation hign performance superplasticizer based on polycarboxylate technology,

high water reduction, high slump retention ability, low alkali content for the product.

It can be widely used in premix of common concrete, gushing concrete, hydro concrete,

also suitable for engineering projects under various weathers and primarily for using

in hot climate area.

Special Features:

1. High water reduction:The water reduction rate of concrete is above 25%-38%

 

2. High slump retention ability:delay time of transporting concrete and time

of detention at construction site

 

3.Excellent workability.high fluidity,easily deposing and compacting          concrete reducing viscosity,without bleeding and segregation, easily pumping.

 

4. Wide adaptability:It is compatible with ordinary silicate cement, silicate cement,

slag silicate cement and all kinds of blendings having excellent dispersibility and plasticity

 

5. Excellent durability: low lacunarate,Low alkali and chlorin-ion content.

Enhancing concrete strength and durability

 

6.Environmental friendly products: No pollution during production

Uses

 

1.Widly used in high strength concrete for railway, haven, traffic, bridge and electric power.

 

2.It is excellent superplasticizer in premix of construction and cast-in-place concrete.

 

3.It is especially suitable for the preparation of  high strength, high durability self-      compacting, steel fiber and self-leveling concrete.

Dosage

 

1. The dosage is suggested as follows (wt.% of cement):0.25%-0.8%.

 

2. It can be mixed in metric water or added in concrete mixer.

The recommended stirring time is 150s at least.

Concrete mixing test should be made before using in order to insure concrete quality.

 

3. It can be compounded together retarder, defoamer, air-entertraing reagent,                                   lignin sulfonic natrium and so on.

4.It is not suggested to use this product directly in concrete or other materials without

formulation blending. The compatibility of this product to particular cement, aggregate

and the other raw materials in the application is not guaranteed.

It should be obtained through trial mixes and formulation technologies by the users.

Technical specification

Items Specification
Visual Appearance Lightyellow viscous liquid
Density (g/cm3,23℃) 1.10±0.01
PH (23℃) 6.0-8.0
Solid content (%) 50.5±1.0
Clˉ(%) ≤0.3
Na2SO4  (%) ≤0.2
Alkali(Na2O+0.658 K2O), % ≤5

Physical properties

It was obtained according to china national standard method P.O.42.5 reference cement,

dosage of  this product was 0.55% by wt of cement

Items Specification Test result
Water Reducing Rate(%) ≥25 30
Ratio of Bleeding Rate (%) ≤60 0
Compressive Strength Ratio (%) 1 d ≥165 220
3 d ≥160 205
7 d ≥150 185
28 d ≥140 150
Air Content(%) ≤5.0 3.0
Slump Retention(60min), mm ≤80 45
Ritio of Shrinkage( 28 d), % ≤120 112
Corrosion of reinforcing steel bar No No
Setting time difference Ini. -90~+120 +90
Fin. +120 +130

Application properties

Test Data-Sheet was obtained according to the China National Standard Method.

The experiment chose standard cement

Packaging

Available in 220kg/ drum or 1000kg/ IBC tank and 23mt flexitank.

Storage

It shall be kept from direst sunlight and stored in dry and cool place at the 0-35℃.

Shelf life

Its shelf life is normally six month.

It is tested eligibility and then used when it is exceeded.

Handling

It is free from alkaline .It is no toxic, hazardous, and corrosive. It is inedible.

 

When it contacts to eyes and skin, The affected area shall be immediately rinsed

with plenty of water for minutes.

 

Consult physician if irritation persists.

 

Keep container closed when it is not in use.

 

Do not store the product directly under sunlight.