Polycarboxylate Superplasticizer (Water reducing)

Polycarboxylate Superplasticizer (Water reducing)

The new generation high water reducing superplasticizer

based on polycarboxylate technology.

  • 描述
  • Inquiry

This product is a new generation high performance & environmental friendly superplasticizer,

It can be widely used in premix of common concrete, gushing concrete, hydro concrete,

high strength concrete, mass concrete and high quality flow plastic concrete etc.


Special Features:


1 A kind of high performance liquid admixture, low-chloride, low-alkali, nontoxic,

free effect on ecological environment.


2 It has excellent water-reducing ability. can greatly reduce slump loss.


3 It  can significantly reduce 25% ~40% mixing water in concrete.


4 High strength enhancing ability. Better performance when used together mineral admixture.


5 No bleeding, anti-segregation, easy to pump and transport.


6 Good appearance of hardened concrete, without water lines, big bubbles, and color difference.


7 A stable performance, non-precipitation.


8 Excellent compatibility with Portland cement.



1 The dosage of this polycarboxylate superplasticizer for normal strength and high strength concrete is

typically 0.6%~1.2% and 1.2%~1.8% respectively, the recommended dosage for GB8076 standard test is 1.0%.
2 The amount used in concrete will be slightly adjusted depending upon job requirements,

such as concrete strength, variations in cement, aggregate and other job site conditions.

Experiments for appropriate dosage must be carried out when changing concrete mix proportion or materials.
3 It can not be compound with naphthalene and anthracene water reducing admixtures.

Experiment must be done when polycarboxylate superplasticizer is used together with other

chemical admixtures and mineral admixtures.


4 It is not suggested to use directly in concrete or other materials without formulation blending.

The compatibility of this product to particular cement, aggregate and the other raw materials

in the application is not guaranteed.


It should be obtained through trial mixes and formulation technologies by the users.


Technical specification


Items Specification
Visual Appearance Lightyellow viscous liquid
Density (g/cm3,23℃) 1.0
PH (23℃) 6.0-8.5
Solid content (%) 50±1.0
Clˉ(%) ≤0.01
Na2SO4  (%) ≤0.2
Alkali(Na2O+0.658 K2O), % ≤5


Physical properties


It was obtained according to china national standard method P.O.42.5 reference cement,

dosage of this product was 0.55% by wt of cement



Items Specification Test result
Water Reducing Rate(%) ≥25 30
Ratio of Bleeding Rate (%) ≤60 0
Compressive Strength Ratio (%) 1 d ≥170 230
3 d ≥160 235
7 d ≥150 220
28 d ≥135 180
Air Content(%) ≤5.0 3.0
Slump Retention(60min), mm ≥150 160
Ritio of Shrinkage( 28 d), % ≤105 102
Corrosion of reinforcing steel bar No No
Setting time difference Ini. -90~+120 +90
Fin. -90~+120 +60


Application properties


Test Data-Sheet was obtained according to the China National Standard Method.

The experiment chose standard cement





Available in 220kg/ drum or 1000kg/ IBC tank and 23mt flexitank.




It shall be kept from direst sunlight and stored in dry and cool place at the 0-35℃.


Shelf life


Its shelf life is normally one year.

It is tested eligibility and then used when it is exceeded.




It is free from alkaline .It is no toxic, hazardous, and corrosive. It is inedible.


When it contacts to eyes and skin, The affected area shall be immediately rinsed with plenty of water for minutes.


Consult physician if irritation persists.


Keep container closed when it is not in use.